High Quality Low Cost Stainless Steel 17-4pH Iron Based Metal Powder for Additive Manufacturing 3D Printing

• Type: Sheet, Heat-Resistant Material
• Standard: ASTM, DIN, ASTM, AISI, GB
• Composition: Ferrous Steel Scrap
• Technique: Cold Rolled, Cold Rolled
• Shape: Plate, Plate
• Surface Treatment: Color Coated, Bright
• Special Use: High-strength Steel Plate, Wear Resistant Steel
• Application: Die Steel Bar
• Refractoriness (℃): 1580< Refractoriness< 1770
• Feature: Long Time Materials, Instant Materials
• Material: Others
• Grade: 300 Series
• Certification: ISO, RoHS, Ibr, AISI
• Specification: as required
• Trademark: as required
• Origin: China
• Production Capacity: 50000mt/Month

Product Description

Even powder composition, less impurities High sphericity Low oxygen content Good flowability High loose density, high tap density

316l Stainless steel powder is widely used in powder silver sintering, pressing, metal injection molding, thermal spraying, metal shot blasting and other industries.

NO.:	304(L)	316(L)	174PH
Production Process	Atomized	Atomized	Atomized
Grade:	304(L)	316(L)	17-4PH
Density	App.4.1-4.5 Tap.>4.9 G/cm3	App.4.1-4.5 Tap.>4.8 G/cm3	App.4.1-4.5 Tap.>4.8 G/cm3
Hardness	34.5HRC	36HRC	35HRC
Size	150um	150um	150um
	75um	75um	75um
	45um	45um	45um
	15um	15um	15um
Content	Cr:18-20 Ni:8-12 C:0.08(0.03) Si:1max Mn:2max Fe:bal.	Cr:16-18 Ni:10-14 Mo:2-3 C:0.08(0.03) Si:1max Mn:2max Fe:bal.	Cr:15.5-17.5 Ni:3-5 Nb:0.15-0.45 Cu:3-5 C:0.07 Si:1max Mn:1max Fe:bal.
Applications	MIM part weight:0.03-200g Apparent relative density>95% Sinter density>7.6g/cm3 sinter temperature:1360-1380c Shrinkage rate:1.18	MIM part weight:0.03-200g Apparent relative density>95% Sinter density>7.8g/cm3 sinter temperature:1360-1380c Shrinkage rate:1.18	MIM part weight:0.03-200g Apparent relative density>95% Sinter density>7.8g/cm3 sinter temperature:1360-1380c Shrinkage rate:1.18