Typical value at 23ºC
|
Unit
|
Test standard
|
N2GF5
|
|
|||
Symbol
|
|
ISO 1043
|
PA66+25%GF
|
Density
|
cm³/g
|
ISO 1183
|
1.32
|
Viscosity
|
ml/g
|
ISO 307
|
145
|
Water absorption ratio, at 23ºC in water saturated
|
%
|
ISO 62
|
6
|
Water absorption ratio,Water saturated
|
%
|
ISO 62
|
1.9
|
|
|||
|
|||
Melting point,DSC
|
ºC
|
DIN 53 765
|
260
|
Melt volum flow rate,MFR
|
cm³/10min
|
ISO 1133
|
-
|
Melt temperature range,injection molding/extrusion
|
ºC
|
|
280-300
|
Mold temperature range,injection molding
|
ºC
|
|
80-100
|
|
|||
Mechanical properties
|
|||
Tensile modulus
|
Mpa
|
ISO 527-1/-2
|
|
Tensile strength, break
|
Mpa
|
ISO 527-1/-2
|
175
|
Tensile elongation, break
|
%
|
ISO 527-1/-2
|
4
|
Bending modulus
|
Mpa
|
ISO 178
|
7600
|
Bending strength
|
Mpa
|
ISO 178
|
260
|
CHARPY impact strength +23ºC
|
KJ/
|
ISO 179/IeU
|
|
CHARPY notched impact strength +23ºC
|
KJ/
|
ISO 179/IeA
|
12
|
izod impact, notch
|
KJ/
|
ISO 180/A
|
|
|
|||
Thermal performance
|
|||
HDT, 1.8 Mpa under load
|
ºC
|
ISO 75-1/-2
|
245
|
HDT, 0.45 Mpa under load
|
ºC
|
ISO 75-1/-2
|
|
|
|
|
|
CLTE, longitudinal/transverse ( 23ºC-80ºC)
|
10-4/K
|
ISO 11359-1/-2
|
0.3
|
Thermal conductivity
|
W/(m.K)
|
DIN 52 612
|
0.33
|
Specific heat volume
|
J/(kg.K)
|
|
1600
|