Commercial Grade Name
|
Iron-Cobalt Alloy ,Hiperco 50 , Hiperco 50A ,Permendur 49
|
Material
|
Iron-Cobalt Vanaduim
|
Standard Specification
|
ASTM A801-14 Alloy 1
|
Surface Finish
|
Cold-Finish
|
I.D. Value
|
200 to 505mm (Paper Coil I.D.)
|
O.D.Value
|
Base on coil weight
|
Edge Finish
|
No Damage
|
Application
|
Stamped lamination assemblies for motors and generators & Turned components for actuators
|
Country of origin
|
China
|
Chemical Compostition,%
|
|||||||||
C
Max
|
Mn
Max
|
Si
max
|
P
Max
|
S
Max
|
Cr
Max
|
Ni
Max
|
Co
|
V
|
Fe
|
0.025
|
0.15
|
0.15
|
0.015
|
0.01
|
0.15
|
0.25
|
47.5-49.5
|
1.75-2.10
|
Bal.
|
Physical Properties
|
|
Resistivity,μΩ•m
|
0.40
|
Density,g/cm3
|
8.12
|
Curie Point,°C
|
940
|
Melting point ,°C
|
1427
|
DC magnetic properties
After magnetic Heat Treating (Final Annealed)
Standard minimum values
|
|||||||
Material
|
Hc
Max.
A/m
|
B at
400
A/m
T
|
B at
800
A/m
T
|
B at
1600
A/m
T
|
B at
2500
A/m
T
|
B at
4000
A/m
T
|
B at
8000
A/m
T
|
Strip Material
|
110
|
1.70
|
2.00
|
2.10
|
2.15
|
2.20
|
2.25
|
Solid Material
|
140
|
1.6
|
1.70
|
1.90
|
2.05
|
2.15
|
2.20
|
Notes:
Hc = coercive field strength, B = induction ,
1) annealed for optimum magnetic properties
2) annealed for optimum mechanical properties
|
|||||||
Typical DC magnetic properties of strip material
After magnetic final annealing (strip material thickness0.35mm)
Typical Values
|
|||||||
Heat treatment temperature, °C
|
µmax
|
Hc
A/m |
B at
800
A/m
T |
B at
1600
A/m
T |
B at
2500
A/m
T |
B at
4000
A/m
T |
B at
8000
A/m
T |
870±5 ºC
|
11940
|
45.85
|
2.177
|
2.271
|
2.313
|
2.354
|
2.389
|
* Typical values measured on rings sample after annealing treatment at 870°C in dry pure hydrogen
Test method: Machining thickness0.35mm strip into 40mm OD and 32mm ID ring shape and final annealing. Then carried out by superposing 20 pieces of ring shape with winding of copper wire to test the material DC magnetic property by magnetic tester. |