High Quality 99.95% Molybdenum Sheet Mo Plate for Heating Elements

• Application: Electronics, Industrial, Aviation, Electronics, Industrial
• Standard: DIN, BS, JIS, DIN, ASTM
• Purity: >99.5%, >99.95%
• Type: Zinc Strip, Molybdenum Plate
• Alloy: Non-alloy, Non-Alloy
• Powder: Not Powder, Not Powder
• Transport Package: Standard Export Packaging
• Specification: as required
• Trademark: as required
• Origin: China
• Production Capacity: 50000mt/Month

Product Description

Product Name	High Quality 99.95% Molybdenum Sheet Mo Plate For Heating Elements
Material	Pure molybdenum and molybdenum alloy
Standard	ASTM B386
Melting Point	2610ºC
Boiling Point	4615ºC
Density	10.2g/cm3
Shape	Sheet, plate, foil, disk, block, round disc
Surface	Polished,bright,cold rolling
Delivery Time	3-15days
Application	1. Molybdenum plate is used for making electric light source parts, components of electric vacuum and electric power semiconductor. 2. It is also used for producing molybdenum boats, heat shield and heat bodies in high temperature furnace.  3. It is widely used in furnace construction mould and parts, electronic components manufacturing and semiconductor industry. In vacuum furnace and high temperature furnace and heat preservation material plate electrode, etc.

Specifications

Thickness   (mm)	Tolerances (mm)	Width     (mm)	Tolerances  (mm)	Length     (mm)	Tolerances (mm)	Flatness   (%)
0.1mm	±0.01	600mm	±1mm	2000mm	±5mm	< 2%
0.2mm	±0.02	600mm	±1mm	2000mm	±5mm	< 2%
0.3mm	±0.02	600mm	±1mm	2000mm	±5mm	< 2%
0.4mm	±0.03	600mm	±1mm	2000mm	±5mm	< 2%
0.5mm	±0.03	600mm	±1mm	2000mm	±5mm	< 2%
0.8mm	±0.05	600mm	±1mm	2000mm	±5mm	< 2%
1mm	±0.06	600mm	±1mm	2000mm	±5mm	< 2%
1.5mm	±0.06	600mm	±1mm	2000mm	±5mm	< 2%
2mm	±0.06	600mm	±1mm	2000mm	±5mm	< 2%
3mm	±0.2	500mm	±1mm	500	±2mm	< 2%
4mm	±0.2	500mm	±1mm	500	±2mm	< 2%

Composition performance parameters of molybdenum products
Type	The main content(%)	The density of(g/cm³)	hardness(HV10)
MGPM	Mo≥99.95	≥10.15	130-180(Recrystallization annealing) 190-280(Stress free annealing)
MGPMLa	Mo:≥99.3:; La2O3:(0.3-0.7)	≥10.1	140-180(Recrystallization annealing) 190-280(Stress free annealing)
MGPTZM	Mo≥99.3 C:(0.01-0.04) O:≤0.05 Ti:(0.4-0.55) Zr:(0.06-0.12)	≥10.05	180-280 HRC(18-28)

 

The thickness of the(mm)	The width of the(mm)	The length of the(mm )	Roughness (Ra)
1.0-3.0	≤300	≤800	0.4-0.8
>3.0-10.0	≤500	≤1000
>10.0	≤300	≤1000