unsaturated polyester resin property
Item |
Range |
unit |
Testing method |
appearance |
Light yellow viscous liquid |
- |
GB/T 8237.4.1.1 |
Acid value |
25-30 |
mgKOH/g |
GB/T 2895 |
Viscosity,25ºC |
0.25-0.45 |
Pa.s |
GB/T 7193.1 |
Solid content |
61-70 |
% |
GB/T 7193.3 |
Gel time ,25ºC |
9-17 |
min |
GB/T 7193-2008 |
Gel time testing: 50% Cyclohexanon peroxide paste: 4%, promoter E1:4%
unsaturated polyester resin casting body property
Item |
Unit |
Measured value |
Testing method |
Barco hardness |
-- |
41 |
GB 3854-83 |
Heat distortion temperature |
ºC |
70 |
GB 1634-04 |
Bending strength |
MPa |
112 |
GB/T 2570-95 |
Tensile Strength |
MPa |
60 |
GB/T 2568-95 |
Elongation at break |
% |
3.5 |
GB/T 2568-95 |
Impact strength |
KJ/m2 |
10.2 |
GB/T 2571-95 |
Notes:1.casting body preparation method according to GB8237-87
2. Curing system: hardener 55%MEKP:2% , promoter E1:2% post cure system: 60ºC×2h + 80ºC×2h
unsaturated polyester resin FRP typical data
Item |
Unit |
Measured data |
Testing method |
Bending strength |
MPa |
365 |
GB/T1449-83 |
Tensile Strength |
MPa |
290 |
GB/T1447-83 |
Impact strength |
KJ/m2 |
235 |
GB/T 1451-83 |
Notes:1.casting body preparation method according to GB8237-87
2.Curing system: hardener 55%MEKP:2% , promoter E1:2% post cure system: 60ºC×3h + 110ºC×3h
unsaturated polyester resin package and storage conditions
ü Packed in metal barrel , 220kg/barrel (about 85.6 gallons)
ü Try to prevent liquid resin from directly sunshine and heat resource
ü Prohibit open before use
ü Flammable, should keep away from open fire
ü Shelf life is 6 month under 25ºC
ü Store and operate in a dry, well-ventilated place
ü Please read MSDS carefully before use this product